BECHEM BERULIT 392

Lubricant for massive forming

Examples of Application
·  Cooling and lubrication in semi hot forging at +680 °C to +950 °C
·  Die forging at +1280 °C
·  Extrusion

Material
·  Non-ferrous metals
·  Steel
·  Stainless steel

Properties
·  Offers anti wear protection
·  Good release effect
·  Graphite free

Characteristic data
·  Service temperature : +120 °C to +300 °C
·  Appearance : transparent

 

Evaporation residue

% 18 – 22

AA_003-153

Density at 20 °C

g/cm3 1.09 – 1.11

AA_003-9 acc. to DIN 51757

Efflux time at 20 °C

s 40 – 60

AA_003-121 acc. to DIN ISO 2431/4

pH value

8.0 – 8.4

DIN 51369

 

Instructions for use

·  Applied on the tools by suitable spraying systems, best by fine atomization

·  After spraying and drying a white effective layer remains on the tool which provides good lubricating and release effect during the forming process

·  Depending on the requirements and severity of the forming process, it should be mixed with water in a ratio from 1:1 up to 1:10

·  Storage : Container to be stored under dry and frost protected conditions. Temperature range +5 °C to +40 °C