BECHEM BERULIT 912 HP

Lubricant for massive forming

Examples of Application
·  Cooling and lubrication in semi hot forging at +680 °C to +950 °C
·  Die forging at +1,280 °C

Material
·  Non-ferrous metals
·  Steel
·  Stainless steel

Properties
·  Offers anti wear protection
·  Good release effect

Characteristic data
·  Service temperature : +120 °C to +350 °C
·  Appearance : black

 

Evaporation residue

% 30 – 35

AA_003-120

Density at 20 °C

g/cm3 1.15 – 1.19

AA_003-9 acc. to DIN 51757

Efflux time at 20 °C

s 20 – 30

AA_003-121 acc. to DIN ISO 2431/6

pH value

10.0 – 11.5

AA_003-33 acc. to DIN 51369

 

Instructions for use

·  Applied on the tools by suitable spraying systems, best by fine atomization

·  After spraying and drying a black effective layer remains on the tool which provides good lubricating and release effect during the forming process

·  Depending on the requirements and severity of the forming process, it should be mixed with water in a ratio from 1:1 up to 1:10

·  Storage : Container to be stored under dry and frost protected conditions. Temperature range +5 °C to +50 °C